It is common for silicone products manufacturers to produce bad phenomena during production, and the causes of unfavorable phenomena are countless. For example, in the case of lack of materials and corners, it can be said that this phenomenon occurs in products produced by many manufacturers every day. It is understood that the factors that will cause this situation to develop in the future are often the most artificial, such as the way of placing materials, controlling the weight of raw materials, etc. After exploring the Dibo silicone products, we have summarized several reasons for the missing corners And processing methods.

The reasons for the lack of materials and corners of silicone products, the wrong way to place the materials is the most serious reason. For products with a core of the middle plate, sometimes it is necessary to place the rubber material up and down and the number of mold holes is too deep. Or if it is too complicated, you need to increase the weight a little more than the original plan. The placement is the most important. So when you place it, you can imagine how to place it so that the rubber can be cured more fully. Phenomenon, machine mold problems, pressure needs to be adjusted during vulcanization process, otherwise not only lack of material, but also unfamiliar phenomenon, the exhaust of the mold during the mold clamping process can not lead to wind and material shortage, If the mold temperature is too high, the rubber material will be burned to death, the raw material will not flow, and the product cannot be cured on time!

For various reasons, the solutions are as follows: the raw materials are placed in a relatively central position, if the material needs to be placed up and down, step by step, if the mold is unreasonable, it can be modified to ensure that the rubber and the mold are properly matched, and an exhaust groove is added. Multi-exhaust, the way of placing the material does not change the method and the method will increase the weight of the raw materials. After leaving the raw materials for more than three days, the vulcanizing agent must be re-mixed to meet the flow requirements after the failure of the raw materials. . The molding process of silicone products is a complex part. Don't compete with the output and speed. Do it first and then do more bad products soon.